SLOW E-225		STANDARD E-224	FAST E-202
	Mixing ratio Volume Weight	2:1 V 100:50P
	Pot-life	3h.			1-1,5h.
	Application viscosity Dilution %	18-20” URKISOL 8229 | URKISOL 3700 5-10%
	Gravity gun Application pressure	1.2-1.4 mm 2-2.5 bar
	Number of coats Total thickness	2 coats 50-60 μm
	Flash time	5-10’ between coats 10 -15’ before baking
	Drying Time 20°C IR Medium wave 60°C	3h 12-15’ 30’			2-2.5h 10-12’ 20’
	Polishing 20°C IR Medium wave 60°C	After drying for 24 h 1h. 1h.

Apply 2 cross coats at 5 to 10-minutes intervals, to allow solvents to evaporate.

For headlight applications, follow the BESA High Resistance Headlight Repair Process.

It is applied directly on the basecoat (both solvent and waterborne) after at least 30 minutes from the application of the basecoat.

When using waterborne basecoats, it is very important to ensure that the water evaporates completely before the clearcoat is applied.
For application on polycarbonate headlights, pre-sand with P800 sandpaper and if necessary with P600. Degrease with plastic cleaning degreaser URKISOL 94.
See the Headlight Repair Process brochure

The use of BESA tack cloths is recommended before applying the clearcoat.

By mixing (by weight) with BESAGLASS HS MATE clearcoat a range of intermediate glosses can be achieved, with a hardener ratio of 2:1 vol.

In order to achieve the glosses shown in the following chart, it is very important to homogenise all the products before mixing them together and the recommended thickness should be between 40-50 my. Thickness below or above these or the use of hardeners other than E-224, may alter the percentages of gloss shown in the chart.

To keep the matt effect of the clearcoat, avoid using abrasive cleaners. Polishing of the clearcoat is not recommended as it would cause an increase in gloss with respect to the rest of the vehicle.

The use of appropriate personal protective equipment is recommended during application, to prevent the irritation of the respiratory tract, skin and eyes. For professional use only.

Keep in a tightly covered container, in a dry and ventilated place, avoiding direct exposure to sunlight. Temperature above 5°C is recommended, between 15 and 30°C optimal.

The VOC content of BESAGLASS HS is a maximum of 840 g/l, in compliance with European Directive 2004/42/EC IIB(E) (840) <840 g/l.

The information contained in this Technical Specification Sheet is based on the knowledge and experience of the BESA technical department, and with it it’s intended to advice and inform, being the responsibility of the user to take the necessary measures to guarantee the intended purpose of the product.
FOR PROFESSIONAL USE ONLY.