BESAGLASS UHS 2K UHS Clearcoat

glass detail uhs besa
General Information
Can size

DESCRIPTION

Ultra-high solids clearcoat specially developed for its application in automotive refinish. It stands out for its easy application, fast drying, excellent gloss, hardness, extensibility, enhancing of metallic effect and resistance to UV rays, as well as very good Car-Wash machines’ abrasion resistance.

HARDENERS

The BESAGLASS UHS clearcoat has a complete range of hardeners to achieve optimum application both for overall and partial repairs (Spot Repair), covering the entire scope of working temperatures.

HardenerTemperature
E-245 Slow>30°C
E-243 Standard20-30°C
E-244 Fast15-25°C
E-247 Extra-Fast10-20°C

COMPLETE VEHICLE PROCESS

APPLICATION

SLOW E-245STANDARD E-243
Mixing ratio
Volume
Weight
2:1 V
100:52 P
2:1 V
100:52 P
Pot-life1-1,5h.1-1,5h.
Application
viscosity
Dilution %
18-20”
URKISOL 8229 | URKISOL 3700
0-5%
Gravity gun
Application pressure
1,3 – 1,4 mm
2-2,5 bar
Number of coats
Total thickness
1,5-2 coats
50-60 μm
Flash time5-10’ between coats
20’ before accelerating drying
Drying Time
20°C
IR Medium wave
60°C
4h
20’
30’
3,5h
20’
30’
Polishing
20°C
IR Medium wave
60°C
8h
1h.
1h.
7,5h
1h.
1h.

Versatile process for any type of repair job, from a partial repair one to the complete repainting of the car, standing out for its high quality, brightness and sharpness of the finishes.

For complete car painting 1.3-1.4 mm fluid peak is recommended.

Apply two crossed coats with an interval of 5 to 10 min. to allow flash-off. Depending on the painting conditions, great results are also possible by applying a lighter plus a full coat.

SURFACE PREPARATION

Sprayed directly over the basecoat (both solvent and water-based) after at least 30 min. from its application.

When using water-based undercoats it is very important to ensure that the water has completely evaporated before applying the clearcoat.

The use of BESA Tack Cloths is recommended before applying it.

MIXING RATIOS

100g250g500g1000g
BESAGLASS UHS66165330660
Hardener3485170340
THINNER (maximum)512.52550

SPOT REPAIR PROCESS - PARTIAL REPAIR

APPLICATION

FAST
E-244
EXTRA-FAST
E-247
Mixing ratio
Volume
Weight
2:1 V
100:52 P
2:1 V
100:52 P
Pot-life30’20-30’
Application
viscosity
Dilution %
18-20”
URKISOL 8229 | URKISOL 3700
0-5%
Gravity gun
Application pressure
1.2-1.3 mm
2-2.5 bar
Number of coats
Total thickness
1.5-2 coats
50-60 μm
Flash time5-10’ between coats
20’ before accelerating drying
Drying Time
20°C
IR Medium wave
60°C
2,5h
15’
20’
1,5h
10-15’
15’
Polishing
20°C
IR Medium wave
60°C
6h
1h
1h
5h
1h
1h

MIXING RATIOS

100g250g500g1000g
BESAGLASS UHS66165330660
HARDENER3485170340
THINNER (maximum)512.52550

RELATED INFORMATION

SAFETY INSTRUCTIONS

The use of appropriate personal protective equipment is recommended during application, to prevent the irritation of the respiratory tract, skin and eyes. For professional use only.

STORAGE

Keep in a tightly covered container, in a dry and ventilated place, avoiding direct exposure to sunlight. Temperature above 5°C is recommended, between 15 and 30°C optimal.

VOC

The VOC content of BESAGLASSS UHS is a maximum of 420 g/l, in compliance with European standard 2004/42/CE IIB(D) (420) <420 g/l.

PRODUCT NOTE

The information contained in this Technical Specification Sheet is based on the knowledge and experience of the BESA technical department, and with it it’s intended to advice and inform, being the responsibility of the user to take the necessary measures to guarantee the intended purpose of the product.
FOR PROFESSIONAL USE ONLY.