C-10 1K SINGLE COAT ANTICORROSION SYSTEM
General Information
DIRECT SYSTEM
CORROSIVITY: C3 | LOW
CORROSIVITY: C3 | LOW
| Support type | Surface pretreatment |
|---|---|
| Steel | Degreased |
| Shotblasted steel | Brushed |
| Iron | Sand-Blasting |
Sectors
Products
¿Quieres obtener más información?
ENVIAR CONSULTADESCRIPTION AND FEATURES
System developed for painting agricultural machinery, public works, commercial vehicles, tanks, pipes, metallic structures, etc. (directly on the substrate). Semigloss finish with easy application, good extensibility, filling power and quick drying.
Good outdoor, water, detergents and petrol resistance.
RESISTANCE AND CERTIFICATES
120 H SALT SPRAY TEST*
An independent approved Laboratory certifies that meets the requirements for category C3 Low in accordance to ISO 12944-2 (Shotblasted Steel Sa 2½).
* This system achieves 300 hours in the Salt Spray Test.
48 H HUMIDITY TEST
PRODUCTS
URKI-NOX
1K DTM Anticorrosion Enamel
| Physical properties | |
|---|---|
| Type of product | Zinc- phosphate special Alkyd |
| Density 20 °C | 1,10 - 1,30 |
| Supply viscosity at 20 °C | 75 - 85 KU (Stormer) |
| Solid Content (% weight) | 60 - 67% |
| Solid Content (% volume) | 48 - 52% |
| V.O.C. | 567 g/l (ready to use) |
| Color | s/m URKI-SYSTEM |
| Features of dry film | |
|---|---|
| Theoretical yield | 12 - 13 m² / l. (40 my) |
| Gloss 60 - 60° | 60 - 85% |
| Recoatability | After 72 hours |
IMPLEMENTATION PROCESS
SURFACE PREPARATION
STEEL
The surfaces should be thoroughly degreased and deoxidized or shotblasted.
APPLICATION
URKI-NOX
20-30" 
URKISOL 222 5-10% 
URKISOL 170 35-40% Ø 1,4-1,6 mm. 
35-45 my 
Non Sticky. 4-5 h. 
URKISOL 170 20-30% 0,011-0,013" 
URKISOL 170 20-30% 0,011-0,013"
General Information
DIRECT SYSTEM
CORROSIVITY: C3 | LOW
CORROSIVITY: C3 | LOW
| Support type | Surface pretreatment |
|---|---|
| Steel | Degreased |
| Shotblasted steel | Brushed |
| Iron | Sand-Blasting |
Sectors
Products