A–05 INDUSTRIAL SYNTHETIC SYSTEM
General Information
1K SYSTEM
CORROSIVITY: C3 | LOW
CORROSIVITY: C3 | LOW
| Support type | Surface pretreatment |
|---|---|
| Steel | Degreased |
| Shotblasted steel | Brushed |
| Iron | Sand-Blasting |
Sectors
¿Quieres obtener más información?
ENVIAR CONSULTADESCRIPTION AND FEATURES
System meant for the painting of metallic structures, boilerwork, agricultural machinery and public works, fork- lifts, cranes, construction material, metal works, where a quality coating to a low cost is required. Stands out for its spreading features, quick drying and high gloss in BESA-VAL.
RESISTANCE AND CERTIFICATES
120 H SALT SPRAY TEST
An independent approved Laboratory certifies that this System meets the requirements for category C3 low in accordance to ISO 12944-2. (Shotblasted steel Sa 21⁄2).
48 H HUMIDITY TEST
The process F- 862 + BESA- VAL has been classified by an external lab as B-s1,d0 according to UNE EN 13501-1:2007 + A1:2010.
PRODUCTS
F-862
Q/D PRIMER FOR STEEL
| Physical properties | |
|---|---|
| Type of product | Modified Alkyd |
| Density 20 °C | 1,55 - 1,75 |
| Supply viscosity at 20 °C | 100 - 120 sec. Ford n.° 4 |
| Solid Content (% weight) | 70 - 76% |
| Solid Content (% volume) | 47 - 53% |
| V.O.C. | 483 g/l (ready to use) |
| Color | Oxyd 8012, Grey 1220, s/m |
| Features of dry film | |
|---|---|
| Theoretical yield | 13 - 15 m² / l. (35 my) |
| Gloss 60 - 60° | Matt < 2% |
| Recoatability | 48 h. |
BESA-VAL
Q/D Industrial Paint
| Physical properties | |
|---|---|
| Type of product | Modified Alkyd |
| Density 20 °C | 0,97 - 1,11 |
| Supply viscosity at 20 °C | 70 - 90 sec. Ford n.° 4 |
| Solid Content (% weight) | 40 - 50% |
| Solid Content (% volume) | 34 - 37% |
| V.O.C. | 598 g/l (ready to use) |
| Color | s/m URKI-SYSTEM |
| Features of dry film | |
|---|---|
| Theoretical yield | 9,5 - 10,5 m2 / l. (35 my) |
| Gloss 60 - 60° | 90 - 95% |
| Recoatability | 24 h. |
APPLICATION PROCESS
SURFACE PREPARATION
STEEL
The surfaces should be thoroughly degreased and deoxidized or shotblasted.
APPLICATION
F-862
20-25'' 
URKISOL 222 10% 
URKISOL 88 15-20% Ø 1,6-1,8 mm. 
30-40 µm 
Non sticky 30 ́ 
5-10 ́ 
URKISOL 88 5-10% 0,011-0,013” 
URKISOL 88 5-10% 0,011-0,013”
BESA-VAL
25±5” 
URKISOL 170/300 20-30% Ø 1,4-1,6 mm. 25±5” 
30-40 my 
Non sticky 2 h. 
URKISOL 170/300 5-10% 0,009-0,011” 
URKISOL 170/300 5-10% 0,009-0,011”
General Information
1K SYSTEM
CORROSIVITY: C3 | LOW
CORROSIVITY: C3 | LOW
| Support type | Surface pretreatment |
|---|---|
| Steel | Degreased |
| Shotblasted steel | Brushed |
| Iron | Sand-Blasting |
Sectors