B-05 SHOP PRIMER EPOXY ACRYLIC SYSTEM
General Information
2K SYSTEM
| Support type | Surface pretreatment |
|---|---|
| Steel | Degreased |
| Stainless steel | Brushed |
| Aluminum | |
| Galvanized | |
| Iron |
Sectors
¿Quieres obtener más información?
ENVIAR CONSULTADESCRIPTION
Designed for a quick painting process with excellent anticorrosion protection and adhesion on all kind of metallic surfaces without sanding. Suitable for capital goods, commercial vehicle, agricultural machinery, etc...
F-286/2 is commonly used as a Bodyshop Primer for its quick drying and recoatability with polyester putties, both with Spatula (Urki-Low, Urki-3000, Urki-Light) or spray gun (Besa-Roc).
BESA-GLASS topcoat stands out for its high body, quick drying, gloss and outdoor resistance.
RESISTANCE AND CERTIFICATES
350 H SALT SPRAY TEST
This system resists 350 hours on the Salt Spray Test in accordance to ISO 9227:2007.
PRODUCTS
F-286/2
2K Epoxy Shop-Primer
| Physical properties | |
|---|---|
| Type of product | Modified Epoxy-Zinc Phosphate |
| Density 20 °C | 1,23 ± 0,05 |
| Supply viscosity at 20 °C | 30 - 35 sec. Ford n.° 4 |
| Solid Content (% weight) | 39 - 43% (mixed with hardener) |
| Solid Content (% volume) | 19 - 23% (mixed with hardener) |
| V.O.C. | 655 g/l (ready to use) |
| Color | Grey Ral 7035, Oxyd 8012 |
| Features of dry film | |
|---|---|
| Theoretical yield | 8 - 9 m² / l. (25 my) |
| Gloss 60 - 60° | Matt 3 - 5% |
| Recoatability | Min 30 min. Recommended 2 h. |
BESA-GLASS
2K Acrylic Enamel
| Physical properties | |
|---|---|
| Type of product | Acrylic- Polyurethane |
| Density 20 °C | 1,00 - 1,30 |
| Supply viscosity at 20 °C | 90 - 100 sec. Ford n.° 4 |
| Solid Content (% weight) | 51 - 61% (mixed with hardener) |
| Solid Content (% volume) | 44 - 48% (mixed with hardener) |
| V.O.C. | 490 g/l (ready to use) |
| Color | s/m URKI-SYSTEM |
| Features of dry film | |
|---|---|
| Theoretical yield | 11 - 12 m² / l (40 my) |
| Gloss 60 - 60° | > 93% |
| Recoatability | 8 h. (To use it as antigraffiti it needs to be sanded and degreased) |
IMPLEMENTATION PROCESS
SURFACE PREPARATION
STEEL, ALUMINIUM, GALVANIZED, STAINLESS STEEL
The surfaces should be thoroughly degreased and deoxidized.
APPLICATION
F-286/2
E-91 
24 h 
15-20" 
URKISOL 357 0-2% Ø 1,4-1,6 mm. 
20-25 my 
Non sticky 15' 
10'
BESA-GLASS
E-225 
3 h 
20-25" 
URKISOL 8229 10-15 % Ø 1,4-1,6 mm. 
40-50 my 
Non sticky 3 h. 
15' 
10-15' 60 ºC/45' (In cabin) 
URKISOL 8229 5-10% 0,009-0,011"