B-10 INDUSTRIAL EPOXY-PUR SYSTEM
General Information
2K SYSTEM
CORROSIVITY: C3 | HIGH
CORROSIVITY: C3 | HIGH
| Support type | Surface pretreatment |
|---|---|
| Steel | Degreased |
| Shotblasted steel | Brushed |
| Aluminum | Sand-Blasting |
| Galvanized | |
| Iron |
Sectors
¿Quieres obtener más información?
ENVIAR CONSULTADESCRIPTION
Paint system specially developed for trailers, semitrailers, tankers, cement mixers, metallic structures, etc...
F-294/2High Solid Primer, formulated with an Epoxy resine and hardened with Polyamide with its high content of antirust pigment offers the system an excellent antirust prection. Suitable for wet on wet application after 20-30 minutes.
Alfapur 3748 topcoat offers excellent elasticity, body, gloss and outdoor resistance.
RESISTANCE AND CERTIFICATES
480 H SALT SPRAY TEST
An independent approved Laboratory certifies that this System meets the requirements for category C3 High in accordance to ISO 12944-2 (Shotblasted Steel Sa 2½).
240 H HUMIDITY TEST
PRODUCTS
F-294/2
2K High Build Epoxy Primer
| Physical properties | |
|---|---|
| Type of product | Zinc Phosphate Epoxy Polyamide |
| Density 20 °C | 1,64 ± 0,05 |
| Supply viscosity at 20 °C | 80 - 90 KU (Stormer) |
| Solid Content (% weight) | 66 - 70% (mixed with hardener) |
| Solid Content (% volume) | 43 - 47% (mixed with hardener) |
| VOC (2004/42/CE) II B. (c) | 514 g/l (ready to use) |
| Color | Grey 7035, Beige 1111 |
| Features of dry film | |
|---|---|
| Theoretical yield | 8 - 9 m² / l. (25 my) |
| Gloss 60 - 60° | Matt Satin 5 - 10% |
| Recoatability | 20 - 30 min. |
ALFAPUR 3748
2K Polyurethane Enamel
| Physical properties | |
|---|---|
| Type of product | Polyester Polyurethane |
| Density 20 °C | 1,00 - 1,20 |
| Supply viscosity at 20 °C | 65 - 90 sec. Ford n.° 4 |
| Solid Content (% weight) | 47 - 56% (mixed with hardener) |
| Solid Content (% volume) | 40 - 42% (mixed with hardener) |
| V.O.C. | 511 g/l (ready to use) |
| Color | s/m URKI-SYSTEM |
| Features of dry film | |
|---|---|
| Theoretical yield | 10 - 11 m² / l (40 my) |
| Gloss 60 - 60° | 90 - 100% |
| Recoatability | 8 h. or 3 h. after cabin drying |
APPLICATION PROCESS
SURFACE PREPARATION
STEEL, ALUMINIUM AND GALVANIZED
The surfaces should be thoroughly degreased and deoxidized or shotblasted.
APPLICATION
F-294/2
E-344 5:1 weight 
24 h 
25-35" 
No dilution. For touch up. 
URKISOL 357 / 394 10-15% Ø 1,6-1,8 mm. 
50-100 my 
Non sticky 45' 
15-30' 80 °C/30 min. (In cabin) 
URKISOL 394 5-10 % 0,013-0,015" 
URKISOL 394 5-10 % 0,013-0,015"
ALFAPUR 3748
E-135 4:1 weight 
>3 h. 
25-30" 
URKISOL 8229 / 3700 25-30% Ø 1,4-1,6 mm 
40-50 my 
Non sticky. 4 h. 
15-30' 70 ºC/30' (In cabin) 
URKISOL 8229 / 3700 0-10% 0,009-0,011" 
URKISOL 8229 / 3700 0-10% 0,009-0,011"
General Information
2K SYSTEM
CORROSIVITY: C3 | HIGH
CORROSIVITY: C3 | HIGH
| Support type | Surface pretreatment |
|---|---|
| Steel | Degreased |
| Shotblasted steel | Brushed |
| Aluminum | Sand-Blasting |
| Galvanized | |
| Iron |
Sectors