B-15 LOW VOC EPOXY-PUR INDUSTRIAL SYSTEM

sistema voc bajo epoxi b15 pur
General Information
2K SYSTEM
CORROSIVITY: C3 | HIGH
Support type Surface pretreatment
Steel Degreased
Shotblasted steel Brushed
Aluminum Sand-Blasting
Galvanized
Iron

¿Quieres obtener más información?

ENVIAR CONSULTA

DESCRIPTION

Paint system specially developed for trailers, semitrailers, tankers, cement mixers, metallic structures,etc...
F-296/2 Ultra High Solid Primer, formulated with an Epoxy resine and hardened with Polyamide with its high content of antirust pigment offers the system an excellent antirust prection. Suitable for wet on wet application after 20-30 minutes.

Alfapur 3790 topcoat offers excellent elasticity, body, gloss and outdoor resistance. This system is compliant with the current legislation in the European Directive 2004/42/CE for Car Refinish. Also used as an alternative to conventional processes for the reduction of VOC emissions, in order to help fulfill the Directive 1999/13/CE .

RESISTANCE AND CERTIFICATES

480 H SALT SPRAY TEST

An independent approved Laboratory certifies that this System meets the requirements for category C3 High in accordance to ISO 12944-2 (Shotblasted Steel Sa 2½).

240 H HUMIDITY TEST

PRODUCTS

F-296/2 2K UHS Epoxy Primer

Physical properties
Type of productZinc Phosphate Epoxy Polyamide
Density 20 °C1,68 ± 0,05
Supply viscosity at 20 °C70 - 75 KU (Stormer)
Solid Content (% weight)66 - 70% (mixed with hardener)
Solid Content (% volume)41 - 45% (mixed with hardener)
V.O.C. (2004/42/CE) II B. (c) (540)456 g/l (ready to use)
ColorCreme 1111
Features of dry film
Theoretical yield8 - 9 m² / l. (25 my)
Gloss 60 - 60°Matt Satin
Recoatability20 - 30 min.

ALFAPUR 3790 2K UHS Polyurethane Enamel

Physical properties
Type of productPolyester Polyurethane
Density 20 °C1,16 - 1,43
Supply viscosity at 20 °C55 - 85 sec. Ford n.° 4
Solid Content (% weight)60 - 67% (mixed with hardener)
Solid Content (% volume)47 - 50% (mixed with hardener)
V.O.C. (2004/42/CE) II B. (d) (420)417 g/l (ready to use)
Colors/m URKI-SYSTEM
Features of dry film
Theoretical yield9 - 10 m² / l (40 my)
Gloss 60 - 60°90 - 100%
Recoatability8 h. or 3 h. after cabin drying

IMPLEMENTATION PROCESS

SURFACE PREPARATION

STEEL, ALUMINIUM AND GALVANIZED
The surfaces should be thoroughly degreased and deoxidized or shotblasted.

APPLICATION

F-294/2
  • E-344 5,5:1 weight
  • 24 h
  • 25-35"
  • No dilution. For touch up.
  • URKISOL 357 / 394 10-15% Ø 1,6-1,8 mm.
  • 50-100 my
  • Non sticky 45'
  • 15-30' 80 °C/30 min. (In cabin)
  • URKISOL 394 3% max. 0,013-0,015"
  • URKISOL 394 3% max. 0,013-0,015"
ALFAPUR 3748
  • E-135 4:1 weight
  • >3 h.
  • 55-65" Air-less 25-30" Spraygun
  • URKISOL 8229 / 3700 5-10% Ø 1,4-1,6 mm.
  • 50-60 my
  • Non sticky. 4 h.
  • 15-30' 70 ºC/30' (In cabin)
  • URKISOL 8229 / 3700 3-5% 0,013-0,015"
  • URKISOL 8229 / 3700 3-5% 0,013-0,015"
General Information
2K SYSTEM
CORROSIVITY: C3 | HIGH
Support type Surface pretreatment
Steel Degreased
Shotblasted steel Brushed
Aluminum Sand-Blasting
Galvanized
Iron

Contact us if you have any question or you can't find the system you were looking for.

Select the download language

Select the download file language