Protection and decoration of gates, bars, lighting masts, raillings, doors and metal structrures.
Due to its formulation based on metallic pigment in laminar structure, it provides an excellent protection for steel and iron exposed to all weather conditions and at the same time has a pleasant look of antique cast iron in several colours. Excellent adhesion and elasticity, without cracking.
Air-less gun: Dilute with 10-15 % vol., for 40-45" Ford n° 4. 100my may be obtained without sagging.
Brush: only for touch-up .
Leve paint settle 15 ́ before painting.
|Density at 20 °C (g/cc)||1,58 ± 0,03|
|Grinding Fineness (μ)||5 - 10|
|Supply viscosity at 20 °C||100 - 120 KU (Stormer)|
|% Solids content (weigth / volume)||65 - 69 % weight; 46 - 50 % volume. (Mixture with hardener)|
|V.O.C. (g/l)||487 (Ready to use) - (2004/42/CE) IIA (j) (500)|
|Type of produtc||Polyester - Polyurethane|
Steel: Sand the metallic surface, or use a scratch brush to remove any rust, clean afterwards with thinner. Prime with F-282/2 2K zinc phosphate primer or F-284/2 2K zinc rich epoxy primer (requires previous shot-blasting) if a better protection is necessary in a maritime or very humid environment.
Galvanized: Previous degreasing and prime with F-286/2 2K epoxy shop-primer or F-282/2 before finishing of with URKI-MIC.
Old layers of paint must be sanded and degreased previously.
|Theoretical yield (m²/l)||9 - 10 (50 my)|
|Gloss 60° - 60°||Matt|
|Second layer||12 h.|
Keep under cover in a cool and well-ventilated place avoiding direct sunlight. Temperatures between 5 and 30 °C recommended.
Can life: 2 years from manufacturing in date its original unopened container. Consult our Technical Department once date has expired.