B-30 INDUSTRIAL AND MARINE HIGH RESISTANCE EPOXY- ZINC- EPOXY HB- PUR SYSTEM
General Information
2K SYSTEM
CORROSIVITY: C5 | HIGH
CORROSIVITY: C5 | HIGH
| Support type | Surface pretreatment |
|---|---|
| Shotblasted steel | Sand-Blasting |
¿Quieres obtener más información?
ENVIAR CONSULTADESCRIPTION
System developed for painting electrical equipments (transformers), wind farms, harbour cranes, and any other product where a High Resistance Standard is demanded.
Alfazinc 1674 EZprovides an excellent protection through its high Zinc metall content. F 294/2 is recoatable with a topcoat wet on wet after 20-30 minutes. URKI-NATO offers excellent properties in hardness, elasticity, resistance to abrasive agents such as soap, fuel, grease, oil, chemical products, etc. Use only with E-225, E-216 or E-202 hardener.
RESISTANCE AND CERTIFICATES
1440 H SALT SPRAY TEST
An independent approved Laboratory certifies that meets the requirements for category C5 I High in accordance to ISO 12944-2 (Shotblasted Steel Sa 2½).
720 H HUMIDITY TEST
URKI-NATO Topcoat is classified as M-1 by an independent approved Laboratory in accodance to UNE 23727:1990.
PRODUCTS
ALFAZINC 1674 EZ
2K Zinc-Rich Epoxy Primer
| Physical properties | |
|---|---|
| Type of product | Zinc-Rich Epoxy Polyamide |
| Density 20 °C | 2,55 ± 0,03 |
| Supply viscosity at 20 °C | 110 - 120 KU (Stormer) |
| Solid Content (% weight) | 80 - 84% (mixed with hardener) |
| Solid Content (% volume) | 51 - 55% (mixed with hardener) |
| V.O.C. | 476 g/l (ready to use) |
| Color | Grey 7000 |
| Features of dry film | |
|---|---|
| Theoretical yield | 9 - 9,5 m² / l (55 my) |
| Gloss 60 - 60° | Mate |
| Recoatability | 1 h. mínimo/máximo: sin límites |
F-294/2
2K High Build Epoxy Primer
| Physical properties | |
|---|---|
| Type of product | Zinc-Phosphate Epoxy Polyamide |
| Density 20 °C | 1,64 ± 0,05 |
| Supply viscosity at 20 °C | 80 - 90 KU (Stormer) |
| Solid Content (% weight) | 66 - 70% (mixed with hardener) |
| Solid Content (% volume) | 43 - 47% (mixed with hardener) |
| V.O.C. | 514 g/l (ready to use) |
| Color | Grey 7035, Beige 1111 |
| Features of dry film | |
|---|---|
| Theoretical yield | 8 - 9 m² / l. (50 my) |
| Gloss 60 - 60° | Matt Satin 5 - 10% |
| Recoatability | 20 - 30 min. |
URKI-NATO
2K Polyurethane Enamel
| Physical properties | |
|---|---|
| Type of product | Polyester Polyurethane |
| Density 20 °C | 1,05 - 1,30 |
| Supply viscosity at 20 °C | 80 - 90 KU (Stormer) |
| Solid Content (% weight) | 55 - 67% (mixed with hardener) |
| Solid Content (% volume) | 48 - 54% (mixed with hardener) |
| V.O.C. | 540 g/l (ready to use) |
| Color | s/m URKI-SYSTEM |
| Features of dry film | |
|---|---|
| Theoretical yield | 12 - 13 m² / l (40 my |
| Gloss 60 - 60° | 95 - 100% |
| Recoatability | 12 h. To use it as antigraffiti it needs to be sanded and degreased. |
IMPLEMENTATION PROCESS
SURFACE PREPARATION
SHOTBLASTED STEEL
The surfaces should be previously shotblasted to Sa 2½ and painted within 3 hours.
APPLICATION
ALFAZINC 1674 EZ
E-305 94:6 weight 
8 h 
Aerográfica 20-30" Airless 30-35" 
URKISOL 357 15-20% Ø 1,6-1,8 mm. 
50-60 my 
Non sticky 3h. 
URKISOL 357 15-20% 0,013-0,015" 
No dilution. For touch up
F-294/2
E-344 5:1 weight 
24 h. 
25-35" 
No dilution. For touch up 
URKISOL 357 / 394 10-15% Ø 1,6-1,8 mm. 
50-100 my 
Non Sticky. 45' 
15-30' 80 ºC/30' (In cabin) 
URKISOL 394 5-10% 0,013-0,015" 
URKISOL 394 5-10% 0,013-0,015"
URKI-NATO
E-277 (indoor) E-225 (outdoor) 
5 h. 
20-22" 
URKISOL 900P / 8229 25-30% Ø 1,4-1,6 mm. 
35-45 my 
Non sticky 3-5 h 
20' 
15-30' 70 ºC/30' (In cabin) 
URKISOL 900/P / 8229 8-12 % 0,009-0,011” 25-35" 
URKISOL 900/P / 8229 8-12% 0,009-0,011” 35-40"
General Information
2K SYSTEM
CORROSIVITY: C5 | HIGH
CORROSIVITY: C5 | HIGH
| Support type | Surface pretreatment |
|---|---|
| Shotblasted steel | Sand-Blasting |