A-15 PHOSPHATANT-PUR SYSTEM
General Information
1K SYSTEM
CORROSIVITY: C3 |
CORROSIVITY: C3 |
| Support type | Surface pretreatment |
|---|---|
| Steel | Degreased |
| Aluminum | |
| Galvanized | |
| Iron |
¿Quieres obtener más información?
ENVIAR CONSULTADESCRIPTION AND FEATURES
System designed for a quick painting process. Designed for painting machinery, indoor and outdoor tanks, etc...F-714is commonly used as a body shop primer due to its rust protection properties. Weldable with no toxic fumes. Not recoatable with Polyester putties. Urki- Nato offers excellent properties in hardness, elasticity, resistance to abrasive agents such as soap, fuel, grease, oil, chemical products, etc.
Can be mixed both with Hardener E-225 (outdoors) or E-277 (indoors).
RESISTANCE AND CERTIFICATES
250 H SALT SPRAY TEST
This system resists 250 hours on the Salt Spray Test in accordance to ISO 9227:2007.
URKI-NATO Topcoat is classified as M-1 by an independent approved Laboratory in accodance to UNE 23727:1990.
PRODUCTS
F-714
Shop-Primer
| Physical properties | |
|---|---|
| Type of product | Modified Vynil |
| Density 20 °C | 0,95 - 1,00 |
| Supply viscosity at 20 °C | 50 - 70 sec. Ford n.° 4 |
| Solid Content (% weight) | 23 - 28% |
| Solid Content (% volume) | 11 - 15% |
| V.O.C. | 774 g/l (ready to use) |
| Color | Grey 1220, Creme 1749, Beige 1639, White 9110, Black Matt 9005 |
| Features of dry film | |
|---|---|
| Theoretical yield | 12 - 14 m² / l. (10 my) |
| Gloss 60 - 60° | Satin 5 - 25% |
| Recoatability | 1 h. |
There is also a possibility of a satin finish using URKI- NATO /SAT instead. Check Technical Data Sheet for mixing ratios Binder/ Hardener as well as the Table for achieving intermediate degrees of gloss.
URKI-NATO
2K Polyurethane Enamel
| Physical properties | |
|---|---|
| Type of product | Polyester Polyurethane |
| Density 20 °C | 1,05 - 1,30 |
| Supply viscosity at 20 °C | 80 - 90 KU (Stormer) |
| Solid Content (% weight) | 55 - 67% (mixed with hardener) |
| Solid Content (% volume) | 48 - 54% (mixed with hardener) |
| V.O.C. | 540 g/l (ready to use) |
| Color | s/m URKI-SYSTEM |
| Features of dry film | |
|---|---|
| Theoretical yield | 12 - 13 m² / l. (40 my) |
| Gloss 60 - 60° | >95% |
| Recoatability | 18 h. (after this time degrease). To use it as antigraffiti it needs to be sanded and degreased. |
There is also a possibility of a satin finish using URKI- NATO /SAT instead. Check Technical Data Sheet for mixing ratios Binder/ Hardener as well as the Table for achieving intermediate degrees of gloss.
IMPLEMENTATION PROCESS
SURFACE PREPARATION
STEEL, ALUMINIUM, GALVANIZED
The surfaces should be thoroughly degreased and deoxidized.
APPLICATION
F-714
15-18" 
URKISOL 88 60-70% Ø 1,6-1,8 mm. 
10-15 my 
Non sticky 20' 
5-10'
URKI-NATO
E-277 (indoor) E-225 (outdoor) 
5 h 
20-22" 
URKISOL 900P / 8229 25-30% Ø 1,4-1,6 mm. 
35-45 my 
Non sticky 3-5 h. 
20' 
10-15' 70 ºC / 30' (In cabin) 
URKISOL 900/P / 8229 8-12% 0,009-0,011” 25-35" 
URKISOL 900/P / 8229 8-12% 0,009-0,011” 30-40"
General Information
1K SYSTEM
CORROSIVITY: C3 |
CORROSIVITY: C3 |
| Support type | Surface pretreatment |
|---|---|
| Steel | Degreased |
| Aluminum | |
| Galvanized | |
| Iron |