"USE ONLY IN INDUSTRIAL FACILITIES"
Acrylic-polyurethane UHS enamel for industrial vehicle painting in single-coat system with an Air-mix equipment of medium pressure.
Elasticity, consistency and good anti-corrosive resistance not needing of a primer.
Good adhesion properties on light metals (aluminum and galvanized steel).
Leave the mixture settle for 15 minutes before starting the application.
(1)High ratio equipments.
|Density at 20 °C (g/cc)||1,17 - 1,35|
|Grinding Fineness (μ)||5 - 10|
|Supply viscosity at 20 °C||75 - 85 KU|
|% Solids content (weigth / volume)||59 % ± 2 weight ; 44% ± 2 vol. (Mixture with hardener)|
|V.O.C. (g/l)||490 (Ready to use)|
|Type of product||Acrylic - Polyurethane / Zinc Phosphate|
|Colour||s/m URKI-SYSTEM, Charts RAL, UNE, NCS, BS, etc|
Steel: The desired surfaces must be properly degreased. In case of looking for a higher corrosion resistance, a Sa 2 1/2 sandblasting is recommended.
|Substrate and material pretreatment||Degreased Steel|
|Mechanical properties||7 days|
|Hardness Persoz||> 150"|
|Erichsen test mm.||7 mm|
|Impact D/I||70 cm D (20 mm ø)|
|Mandrel bend||6 mm ø|
|Adhesion||Gt-0 (Steel, galvanized steel and aluminum)|
|Theoretical yield (m²/l)||5 - 6 (80 my)|
|Gloss 60° - 60°||70-80 %|
|Second layer||24h air / 3 h. after spray-booth drying|
By mixing (on weight) with the ALFA-PUR 3799 binder, intermediate gloss ranges can be attained.
For the achievement of the different gloss degrees on the following table, it is very important to homogenize all the products before being mixed between them.
|Gloss 60° - 60°||50-60||40-50||35-40||30-35||25-35|
The values shown in the tables are for guidance only and with the recommended thickness (70-100 my)
|Resistance according to ISO 12944-2||C3 HIGH|
Keep under cover in a cool and well-ventilated place avoiding direct sunlight. Temperatures between 5 and 30 °C recommended.
Can life: 2 years from manufacturing in date its original unopened container. Consult our Technical Department once date has expired.